Fracture damage of two dimensional C/SiC composites under dynamic loading

The dynamic tensile properties of 2D C/SiC composites were investigated by means of Split Hopkinson Tensile Bar (SHTB) and ultra high-speed camera.Based on its macro mechanic behavior,the failure process of the specimen under dynamic tensile loading was analyzed.The experimental results indicate that the stress-strain curve is obviously non-linear,and examination of the failure process of the specimen helps define the four phases of crack propagation,namely,the damage accumulation phase,crack initiation phase,yield failure phase and crack fast spreading phase.